底板形态和粘结时间对托槽粘结强度的影响

山东大学学报(医学版) ›› 2013, Vol. 51 ›› Issue (10): 38-41.

底板形态和粘结时间对托槽粘结强度的影响

王宁1，付传芸1，杨瑞2，赵刚3，潘淑勤1

1.山东大学附属省立医院口腔正畸科，济南 250021；
2.山东大学附属济南市中心医院口腔科，济南 250013；
3.莱芜市中医医院口腔科，山东莱芜 271100

收稿日期:2013-07-25 出版日期:2013-10-10 发布日期:2013-10-10
通讯作者: 付传芸， E-mail:cloudfcy@163.com

Influence of base forms and bond time on the shear bond strength of orthodontic brackets

WANG Ning1， FU Chuan-yun1， YANG Rui2， ZHAO Gang3， PAN Shu-qin1

1. Department of Orthodontics, Shandong Provincial Hospital Affiliated to Shandong University, Jinan 250021, China;
2. Department of Stomatology, Jinan Central Hospital Affiliated to Shandong University, Jinan 250013, China;
3. Department of Stomatology, Laiwu City Hospital of Traditional Chinese Medicine, Laiwu 271100, Shandong, China

Received:2013-07-25 Online:2013-10-10 Published:2013-10-10

摘要/Abstract

摘要：

目的对目前正畸临床上最常用的金属网底托槽和微蚀刻底托槽的粘结强度进行对比分析，并确定力加载的适宜时间。方法选取正畸临床上减数拔除的上颌第一前磨牙120颗，随机分为2组，第1组粘结金属网底托槽，第2组粘结金属微蚀刻底托槽。每组分别在粘结后5min、10min、15min、30min、60min、24h测定抗剪切强度(SBS)，并统计粘结剂残留指数(ARI)，电镜扫描托槽粘结前、脱落后底板形貌。结果金属网底托槽组和微蚀刻底托槽组SBS均随粘固时间的延长而增大，24h时粘结强度最大，且与其他时间点有统计学差异(P<0.05)。结论两种金属托槽的粘结强度均能满足临床需要，可在托槽粘结后5min进行正畸力的加载。

关键词: 托槽；粘结强度；抗剪切强度；粘结剂残留指数

Abstract:

Objective To find the appropriate time to load the bracket by comparing the shear bond strengths (SBS) of two kinds of brackets with different bases. Methods One hundred and twenty extracted youth first premolars were divided into 2 groups randomly. The standard straight wire brackets with spherical mesh base and etching base were used in the 2 groups respectively. The SBS test for the 2 groups was performed at different debond times of 5, 10, 15, 30 and 60 minutes and 24 hours. The chi-squared test was also used to determine the significant differences for the adhesive remnant index (ARI) scores between the 2 groups. Scanning electronic microscope was used to observe the shape of the brackets with different bases before bonding and after debonding from teeth. Results The highest shear bond strength was obtained at the debond time of 24 hours for the both kinds of metal brackets, which had significant difference than those at other times (P<0.05). Conclusion The both kinds of metal brackets are strong enough to meet the clinical needs. It is reliable to load the bracket 5 minutes after it is bonded.

Key words: Bracket; Bond strengths; Shear bond strengths; Adhesive remnant index

中图分类号:

R783.5

王宁1，付传芸1，杨瑞2，赵刚3，潘淑勤1. 底板形态和粘结时间对托槽粘结强度的影响[J]. 山东大学学报(医学版), 2013, 51(10): 38-41.

WANG Ning1， FU Chuan-yun1， YANG Rui2， ZHAO Gang3， PAN Shu-qin1. Influence of base forms and bond time on the shear bond strength of orthodontic brackets[J]. JOURNAL OF SHANDONG UNIVERSITY (HEALTH SCIENCES), 2013, 51(10): 38-41.

参考文献

相关文章 14

[1]	刘盼盼1,2，谢志伟1,2，李国菊2,3，郭泾1,2. 汉族均角成年人群下颌体形态的测量分析[J]. 山东大学学报(医学版), 2013, 51(12): 95-99.
[2]	王娜娜，曹丛，刘东旭. 前方前牵引矫治前牙反牙合后下颌位置的变化[J]. 山东大学学报(医学版), 2013, 51(9): 95-99.
[3]	张梅1，席兰兰2，王旭霞3，张君3. 牙周病重建牙周和正常牙周对正畸力反应差异性的实验研究[J]. 山东大学学报(医学版), 2013, 51(7): 28-31.
[4]	丛淑敏1，王旭霞2，张丽娜2，李涛2，王胜林3，李静2，张君2,4. 伊班膦酸钠在正畸源性根吸收中对破骨细胞的影响[J]. 山东大学学报(医学版), 2012, 50(9): 44-49.
[5]	杜林娜1，郭泾2. 口腔矫治器治疗OSAS有效者和无效者的比较[J]. 山东大学学报(医学版), 2012, 50(8): 120-123.
[6]	谢志伟1，王凡涛2，郭泾1，3. 第二恒磨牙生长萌出位置和发育阶段与不同矢状骨面型的相关性研究[J]. 山东大学学报(医学版), 2012, 50(5): 75-.
[7]	王磊1，张梅2，王旭霞3，王媛3，张君1,3. 中药川续断促进再生牙周对正畸力反应的研究[J]. 山东大学学报(医学版), 2011, 49(11): 18-.
[8]	王蕊蕊，刘洪，刘东旭. 基于三维图像识别颅面部标志点的准确性及可靠性评价[J]. 山东大学学报(医学版), 2011, 49(9): 83-.
[9]	薛涵1，杜文婷2，郭泾3. 正畸加载对自体移植牙预后影响的显微CT研究[J]. 山东大学学报(医学版), 2010, 48(10): 29-33.
[10]	张燎1，诸葛春耕1，梅银生2，张君2. 不同正畸力作用下牙周组织中碱性成纤维细胞生长因子表达的实验研究[J]. 山东大学学报(医学版), 2010, 48(1): 34-37.
[11]	. 拔牙创不同愈合期对磨牙远移影响的三维有限元分析[J]. 山东大学学报(医学版), 2009, 47(10): 68-71.
[12]	. 应用PAR指数评价不同矫治技术的治疗效果[J]. 山东大学学报(医学版), 2009, 47(7): 78-80.
[13]	. 牙槽骨牵张快速移动正畸牙齿对牙髓中TNFα含量影响的实验研究[J]. 山东大学学报(医学版), 2009, 47(9): 36-39.
[14]	靳淑梅1，王旭霞1，3，张丽娜1，任旭升1，2，张君1，3. 不同工况下埋伏牙的位移趋势及牙周应力的三维有限元分析[J]. 山东大学学报(医学版), 2010, 48(12): 67-74.

多维度评价

Viewed

Full text

Abstract

Cited

Shared

Discussed